Slotheater

Warm compaction of metal powder

Warm compaction gives a major advantage compared to the conventional "cold" compaction by producing changes in the pore morphology of sintered parts.
The result is that higher density levels are achieved and, at the same time, warm compaction products have more even density distributions, i.e. less variation in density within a component.
 
The warm compaction process is applicable to most powder/material systems. This will lead to higher strength and better dimensional tolerances. A possibility of green machining is also obtained by this process partly due to high green strength.
 
The Slot heater can be fitted to all press types and is manufactured and marketed under licens from Höganäs AB, Sweden.

 

The process offers:

  • An increase in green density and strength 
  • Between 0,1-0,3g/cm3
  • Improved powder flow
  • Reduction in green scrap caused by damage
  • Increased potential for machining in green state

 

Lower compacting
pressures will:

  • Extend tool life
  • Reduce the likelyhood of tool breakage
  • Facilitate multi-impression tooling

 

Technical specifications:

  • Capacity at 130°C – max 4,5 kg/min
  • +/- 2°C temperature control
  • Pre-heating timer, approx. 1 hour
  • 3x400V 50Hz 32A power requirement
  • Simple installation of the heating elements
    (max 3,5 kW/unit) and thermocouples converts the system ready for production.

In addition to the powder heater, temperature regulators and tyristor units are included for:

  • Punch
  • Die
  • Fillshoe
  • Bottom plate

 

Safety features:

  • Separate breakers for all heating circuits
  • Overheat protection for the oil system
  • Low temperature alarm
  • Earth fault switch
  • Emergency stop

slotheater